Metal and Non-Metal Modified Titania: the Effect of Phase Composition and Surface Area on Photocatalytic Activity

The application of TiO2 photocatalysis in various environmental fields has been extensively studied in the last decades due to its ability to induce the degradation of adsorbed organic pollutants. In the present work, TiO powders doped and co-doped with sulfur and nitrogen and modified with platinum were prepared by particulate sol-gel synthesis. PXRD measurements revealed that the replacement of HCl with H2SO4 during synthesis reduced the size of the crystallites from similar to 30 nm to similar to 20 nm, increasing the surface area from similar to 44 m(2)/g to similar to 80 m(2)/g. This is consistent with the photocatalytic activity of the samples and the measured photocurrent behavior of the photocatalysts. The results showed that the properties of the powders (i.e., surface area, crystallite size, photocurrent behavior) depend strongly not only on the type but also on the amount of acid and dopants used in the synthesis. Doping, co-doping and modification of TiO2 samples with nitrogen, sulfur and platinum increased their photocatalytic activity up to 6 times.

Automated summary

This study successfully prepared sulfur and nitrogen co-doped and platinum modified titanium dioxide powders with high photocatalytic activity by controlling the type and amount of acid and dopants used in the synthesis. The changes in surface area and crystallite size were consistent with the photocatalytic activity and photocurrent behavior.