期刊
MATERIALS & DESIGN
卷 105, 期 -, 页码 240-250出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.matdes.2016.05.058
关键词
Low alloy steel; Welded joint; Pitting corrosion; Modelling
资金
- National Natural Science Foundation of China [51325504]
- Program of Shanghai Subject Chief Scientist [14XD1401300]
Pit initiation and growth in a 25Cr2Ni2MoV welded joint in the simulated environment of a low pressure nuclear steam turbine was addressed by using U-bend samples. Different pit densities in various zones of the welded joint were observed with the order: weld near heat affected zone > base metal near heat affected zone > heat affected zone. This was partly ascribed to the galvanic effect and material difference. Pits in the base metal emanated from local deep grooves of surface machining, while they nucleated from surface inclusions in weld metal. A model for pit distribution of the welded joint was developed and verified accordingly. (C) 2016 Elsevier Ltd. All rights reserved.