This study investigated the effect of heat treatment parameters on the microstructure, defects, and hardness of an Al-16Si-6Cu die-cast alloy. It was found that lower solution treatment temperature and shorter ageing time resulted in lower pore area fraction, smaller pores, and finer primary silicon particles with higher circularity.
The current study investigated the effect of heat treatment parameters, including solution treatment temperature (STT), time, and quench rate, on the microstructure, defects, and hardness of an Al-16Si-6Cu Shift fork die-cast alloy. The changes in primary silicon particle (PSP) features were examined quantitatively by optical microscopy, coupled with image analysis and SEM equipped with EDS. The biggest PSPs (27 +/- 8 mu m) and the highest area fraction (23%) were found in the sample solution treated at 470 degrees C and cooled in the furnace. The hardness value increased in heat-treated samples slightly (140-148 BHN). A lower STT (420 degrees C) and a lower ageing time (1 h) are suitable conditions for the heat treatment of an Al-16Si-6Cu die-cast alloy, in which a lower pore area fraction, 1.18, smaller pore, 4.5 mu m, along with finer primary silicon, 9.5 +/- 3 mu m, with higher circularity, 0.38 +/- 0.04, was achieved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据