Pd-Multi@HCS catalysts with Pd nanoparticles partially embedded in the inner wall of hollow carbon spheres were synthesized by a hard template method. The influence of the pore structure of the hollow carbon shell on the catalytic performance for the direct synthesis of H2O2 from H-2 and O-2 was systematically researched. The results showed that the special hollow structure with a large number of micropores ensured the maximum exposure of Pd active sites and improved the catalytic activity and stability of the Pd-Multi@HCS catalysts.
Pd-Multi@HCS catalysts with Pd nanoparticles partially embedded in the inner wall of hollow carbon spheres were synthesized by a hard template method. The synthesis process of Pd-Multi@HCS catalysts and the influence of the pore structure of the hollow carbon shell on the catalytic performance for the direct synthesis of H2O2 from H-2 and O-2 were systematically researched in this work. When the mass ratio of resorcinol (R) and formaldehyde (F) was R/F = 0.20 g/0.286 g, the mass of CTAB was 2.0 g, and the additional amount of 0.075 M H2PdCl4 solution was 1.0 ml; Pd nanoparticles obtained by in situ reduction using freshly prepared NaBH4 solution with an average size of 6.7 nm showed good dispersion and partial embedding in the inner wall of the hollow carbon shell. The average size of cavity diameter and the hollow carbon shell thickness were 145 nm and 8.03 nm, respectively. More importantly, there were a large number of micropores with a pore size distribution of 1.5 nm in the hollow carbon shell. This special hollow structure ensured the maximum exposure of Pd active sites and the optimal transfer and diffusion ability, which were conducive to improving the catalytic activity and stability of the Pd-Multi@HCS catalysts.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据