THERMAL SCIENCE
卷 26, 期 4, 页码 2885-2893出版社
VINCA INST NUCLEAR SCI
DOI: 10.2298/TSCI2204885K
关键词
pulse plating; Ni-W; PTFE electrodeposition; microhardness; tribological behavior
资金
- Research Fund of the Sakarya University of Applied Sciences [2021-50-02-029]
The Ni-W/PTFE co-depositions were successfully prepared on steel using pulse electrodeposition methods. The best microstructure and wear performance were achieved at a PTFE concentration of 15 g/L.
The Ni-W/PTFE co-depositions were successfully prepared on steel via pulse electrodeposition methods. Electrodeposition was perform by dispersing 5-20 g/L PTFE particles from Ni-Watt bath. The surface morphology, phase analyses crst-alytallite size, distorsion and hardness of the samples were characterized by SEM, XRD, and Vicker???s microhardness tester. The friction coefficient of the coatings were carried out using CSM microtester. As increasing with the concentration of the PTFE in the solution, the wear resistance properties of theco-depositions were increased. These experimental results determined that the PTFE concentration of 15 g/L in the electrolyte was the optimum content to obtain the best micro-structure and wear performance.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据