COMPOSITES SCIENCE AND TECHNOLOGY
卷 113, 期 -, 页码 31-37出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.compscitech.2015.03.013
关键词
Carbon fibers; Polymer-matrix composites (PMCs); Electrical properties; Carbon black
资金
- National Natural Science Foundation of China [51373171, 21204079, 51233005, 21374114]
In this work, carbon black (CB) was introduced into polypropylene/carbon fiber (PP/CF) composite to fabricate multifunctional composites with the improved thermal stability, flame retardancy and electrical conductivity. The morphology investigation showed that one-dimensional CF and zero-dimensional were well dispersed in the PP matrix, and the multistage structure was formed in PP matrix. Compared to pristine PP, the maximum weight loss temperature under air atmosphere was enhanced by 79 degrees C. The peak value of the heat release rate measured by a cone calorimeter was significantly reduced by 70%, and the total heat release decreased from 198 to 166 MJ/m(2). The dramatically enhanced flame retardancy of PP composites was attributed to the formation of a strong three-dimensional (3D) network structure in PP matrix where one-dimensional CF acted as bridges connecting individual zero-dimensional CB, and the accelerated oxidation crosslinking reaction of PP radicals by CB and CF. Furthermore, the electrical conductivity of PP composites was significantly enhanced to 7.8 S/m due to the formation of 3D conductive pathways from CB and CF within the matrix. (C) 2015 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据