In the present study, graphene nanoribbon was prepared through unzipping the multi walled carbon nanotubes, and its reinforcing effect as a filler to the silicone rubber was further investigated. The results showed that carbon nanotubes could be unzipped to graphene nanoribbon using strong oxidants like potassium permanganate and sulfuric acid. The prepared graphene nanoribbon could homogeneously disperse within silicone rubber matrix using a simple solution mixing approach. It was also found from the thermogravimetric analysis curves that the thermal stability of the graphene nanoribbon filled silicone rubber nanocomposites improved compared to the pristine silicone rubber. Besides, with the incorporation of the nanofiller, the mechanical properties of the resulting nanocomposites were significantly enhanced, in which both the tensile stress and Young's modulus increased by 67% and 93% respectively when the mass content of the graphene nanoribbon was 2.0 wt%. Thus it could be expected that graphene nanoribbon had large potentials to be applied as the reinforcing filler to fabricate polymers with increased the thermal and mechanical properties. (C) 2014 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据