Anisotropic dispersion promoting and passivation protecting of CA@JNs@Zn2+ Janus nanosheets on epoxy anticorrosive coatings

Defects in the curing process of epoxy coatings tend to deteriorate the anticorrosion performance of the coatings. An important way to enhance the anticorrosion performance of epoxy coatings is to add flaky fillers. In this paper, anisotropic Janus nanosheets (JNs) were prepared and modified by cardanol (CA) and Zn2+. Then, the obtained CA@JNs@Zn2+ Janus composite nanosheets were introduced into epoxy coatings. When the content of CA@JNs@Zn2+ is 0.2 %, the mechanical properties and corrosion resistance of the coating were effectively improved. The tensile strength of 0.2 %-CA@JNs@Zn2+/EP coating is 79 % higher than that of pure epoxy coating. The EIS analysis showed that the low-frequency impedance of the coating remained as high as 16.45 Gohm & BULL;cm2 after 35 days of immersion, and remained above 10 Gohm & BULL;cm2 during the whole immersion period, which demonstrating the optimal corrosion resistance. This paper provides a theoretical basis for the preliminary application of Janus material in the field of anticorrosion, and the prepared composite coatings are expected to be used for anticorrosion in harsh environment.

Automated summary

Anisotropic Janus nanosheets modified with cardanol and Zn2+ were added to epoxy coatings, improving the mechanical properties and corrosion resistance of the coatings.