This study proposed a facile and efficient method for the dissolution of zinc ferrite using sulfuric acid leaching assisted by copper powder. The results showed that zinc ferrite could be completely dissolved under certain conditions, with the shortest dissolution time of 10 minutes. The leaching kinetics study revealed that the leaching process of zinc ferrite was controlled by surface chemical reaction.
Zinc ferrite is a dominant phase in mass solid wastes generated from zinc or iron production, which causes the obstacle of metal recovery and recycling. A facile and efficient sulfuric acid leaching process of zinc ferrite assisted by copper powder was proposed in this study. The effects of factors on the leaching of zinc ferrite and copper were investigated. The results showed that zinc ferrite and copper were coupled and leached. The complete dissolution of zinc ferrite was obtained with wide ranges of leaching conditions. The shortest time for the complete dissolution of zinc ferrite was 10 min at 80 degrees C under the conditions: copper to zinc ferrite molar ratio of 1.5, sulfuric acid concentration of 100 g/L, liquid to solid ratio of 30 mL/g, and copper powder of + 38.5-20 mu m. The least consumption of copper to realize the complete dissolution of zinc ferrite was 27.15%. The leaching kinetics was studied by the shrinking core model. It was found that zinc ferrite leaching assisted by copper was controlled by surface chemical reaction. The apparent activation energies for zinc, iron, and copper are 56 kJ/mol, 56 kJ/mol, and 50 kJ/mol, respectively. Characterization of the leaching residues and deter-mination of iron and copper species in the leaching solution showed galvanic corrosion took place between zinc ferrite and copper, enhancing their acid dissolution.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据