Characterization of crack-free AA-7075 fabricated by laser powder bed fusion with addition of Zr50.7Cu28Al12.3Ni9 metallic glass

期刊

MATERIALS LETTERS
卷 353, 期 -, 页码 -

出版社

ELSEVIER
DOI: 10.1016/j.matlet.2023.135283

关键词

3D printing; Metallic composites; Microstructure; Metallic glass; Hot cracks

向作者/读者索取更多资源

The inclusion of 2 wt% Zr50.7Cu28Al12.3Ni9 metallic glass powders successfully eliminated hot cracks in AA-7075 specimens fabricated by laser powder bed fusion. Microstructure analysis revealed significant grain refinement in the AA-7075/MG specimen due to the formation of Al3Zr precipitates. The average grain size reduced from 9.26 μm to 1.6 μm, and the previously coarser columnar grains transformed into finer equiaxed grains with random orientation.
The inclusion of 2 wt% Zr50.7Cu28Al12.3Ni9 metallic glass (MG) powders successfully eliminated the hot cracks in AA-7075 specimens fabricated using laser powder bed fusion (LPBF). The microstructure analysis revealed a significant enhancement in grain refinement within the AA-7075/MG specimen as a result of the formation of Al3Zr precipitates. The average grain size reduced from 9.26 mu m to 1.6 mu m, and the previously coarser columnar grains transformed into finer equiaxed grains with random orientation. Moreover, the AA-7075/MG specimen demonstrated a noteworthy microhardness exceeding 160 HV. With an elongation of about 7.2%, the highest ultimate tensile stress and yield strength are 488.7 MPa and 460.8 MPa, respectively.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.6
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据