Effect of ceria particle size as intermediate layer for preparation of composite Pd-membranes by electroless pore-plating onto porous stainless-steel supports

The use of H-2-selective membranes for ultra-pure H-2 production has been assigned as an attractive technology, particularly those based on Pd-films deposited onto porous stainless-steel (PSS) supports. The ability to incorporate thin Pd-films with enough adherence on any internal or external surfaces becomes essential to minimize their complexity and cost while improving their performance. The modification of original PSS substrates with diverse intermediate layers, especially those made of ceria, is presented as a promising alternative. In this context, the current study addresses for the first time the use of different CeO2 particle sizes to generate an intermediate layer and facilitate the subsequent generation of a thin Pd-film by electroless pore-plating (ELP-PP). The membrane containing the smallest CeO2 particle size (membrane S) demonstrated the lowest performance, which was assigned to the high compaction of the material and generation of cracks on its surface during calcination that consequently led to the deposition of a greater amount of Pd. On the other hand, the morphology of membranes M (medium CeO2 particle size) and L (large CeO2 particle size) were very similar, although the first one demonstrated a slightly smaller interparticle porosity, which led to the deposition of a more homogeneous and thinner Pd-film. Therefore, an outstanding performance in terms of H-2 permeance (5.98 x 10(-4) mol.m(-2).s(-1).Pa-0.5 at 400 degrees C) was obtained for this membrane. Permeation tests with binary mixtures (H-2-N-2, H-2-CO2, or H-2-CO) revealed a concentration-polarization effect in all cases, as well as a certain inhibition effect in the presence of CO. Finally, it should be highlighted the high stability of the membranes during the entire set of experiments, independently of the considered particle size. Thus, enough mechanical and thermal resistances can be assured for future applications.

Automated summary

This study investigates the use of different sizes of CeO2 particles to generate an intermediate layer and facilitate the deposition of a thin Pd-film on H-2 selective membranes. Membrane M demonstrates the best performance in terms of H-2 permeance, and the stability of the membranes is high regardless of the particle size.