Biosorption of rare earth elements from luminophores by G. sulphuraria (Cyanidiophytina, Rhodophyta)

Lanthanides are indispensable constituents of modern technologies and are often challenging to acquire from natural resources. The demand for REEs is so high that there is a clear need to develop efficient and eco-friendly recycling methods. In the present study, freeze-dried biomass of the polyextremophile Galdieria sulphuraria was employed to recover REEs from spent fluorescent lamps (FL) luminophores by pretreating the freeze-dried biomass with an acid solution to favour ion exchange and enhance the binding sites on the cell surface available for the metal ions. Lanthanides were extracted from the luminophores using sulfuric acid solutions according to standardised procedures, and the effect of biosorbent dosage (0.5-5 mg/ml) and biosorption time (5-60 min) were evaluated. The content of individual REEs in the luminophores and the resulting algal biomass were determined using inductively coupled plasma mass spectrometry (ICP-MS). The most abundant REE in the luminophores was yttrium (287.42 mg/g dm, 91.60% of all REEs), followed by europium (20.98 mg/g, 6.69%); cerium, gadolinium, terbium and lanthanum was in trace. The best biosorption performances were achieved after 5 min and at the lowest biosorbent dosage (0.5 mg/mL). The highest total metal amount corresponded to 41.61 mg/g dried mass, and yttrium was the most adsorbed metal (34.59 mg/g dm, 82.88%), followed by cerium (4.01 mg/g); all other metals were less than 2 mg/g. The rapidity of the biosorption process and the low biosorbent dosage required confirmed this microalga as a promising material for creating an ecosustainable protocol for recycling REEs.

Automated summary

Lanthanides are essential for modern technologies and difficult to obtain from natural resources. Therefore, efficient and eco-friendly recycling methods are in high demand. In this study, a polyextremophile microalga was used to recover lanthanides from spent fluorescent lamps. The best recovery performance was achieved with a low dosage of the biosorbent and a short biosorption time.