Structure and thermal behavior of biobased vitrimer of lactic acid and epoxidized canola oil

Biobased vitrimers were obtained from epoxidized canola oil (ECO) and lactic acid (LA) using zinc acetate (ZnAc) and ZnAl-layered double hydroxide (ZnAl) in the proportions of 1 and 2 wt% as transesterification catalysts. Reactions containing ECO and LA showed an average enthalpy of cure of approximately 85 mJ mg-1 and materials cured in the presence of the catalysts showed lower enthalpies of cure and decrease in the material gel content. ECO-LA reaction generated materials with rubber-like properties with Tg ranging from -15 degrees C to -23 degrees C, where the material without a catalyst showed the higher Tg value. The presence of catalysts gave the material vitrimer properties, with the softening point associated with transesterification reactions and topology freezing temperature transition at temperatures (Tv) between 195-235 degrees C. Biobased vitrimers were obtained from epoxidized canola oil (ECO) and lactic acid (LA) using zinc acetate (ZnAc) and ZnAl-layered double hydroxide (ZnAl) in the proportions of 1 and 2 wt% as transesterification catalysts.

Automated summary

Biobased vitrimers were successfully obtained by using zinc acetate and ZnAl-layered double hydroxide as transesterification catalysts for the reaction between epoxidized canola oil and lactic acid. The presence of catalysts led to lower enthalpies of cure and decreased material gel content, resulting in materials with rubber-like properties.