Thermodynamic effects after Diode and Er:YAG laser irradiation of grade IV and V titanium implants placed in bone - an ex vivo study. Preliminary report

Many inserted implants are affected by peri-implantitis. The aim of our study was to evaluate increases in implant temperature, depending on the diameter and chemical composition of implants. In particular we measured the time it takes for the temperature of an implant to rise by 10 degrees C and evaluated laser power settings required to prevent thermal injury when an implant surface is decontaminated during the treatment of peri-implantitis. The study analysed six implants placed in porcine ribs and divided into two groups according to their diameter and chemical composition (grade IV and grade V titanium). The implants were irradiated with Diode and Er:YAG lasers using different laser parameters. The temperature was measured with a K-type thermocouple. The temperature on the implant surface rose as the laser power increased and the implant diameter decreased. The time required to increase the temperature of an implant by 10 degrees C was less than it was for titanium grade IV. The temperature gradient was below 10 degrees C for all implants treated using a laser power up to 1 W. It is important to choose the correct laser parameters, depending on the chemical composition and diameter of the implant, so that decontamination of the implant surface is thorough, effective and safe.