Rapid Intrafibrillar Mineralization Strategy Enhances Adhesive-Dentin Interface

Biomimetic mineralization of dentin collagen appears to be a promising strategy to optimize dentin bonding durability. However, traditional postbonding mineralization strategies based on Ca/P ion release still have some drawbacks, such as being time-consuming, having a spatiotemporal mismatch, and having limited intrafibrillar minerals. To tackle these problems, a prebonding rapid intrafibrillar mineralization strategy was developed in the present study. Specifically, polyacrylic acid-stabilized amorphous calcium fluoride (PAA-ACF) was found to induce rapid intrafibrillar mineralization of the single-layer collagen model and dentin collagen at just 1 min and 10 min, as identified by transmission electron microscopy, scanning electron microscopy, and atomic force microscopy. This strategy has also been identified to strengthen the mechanical properties of demineralized dentin within a clinically acceptable timeframe. Significantly, the bonding strength of the PAA-ACF-treated groups outperformed the control group irrespective of aging modes. In addition, the endogenous matrix metalloproteinases as well as exogenous bacterial erosion were inhibited, thus reducing the degradation of dentin collagen. High-quality integration of the hybrid layer and the underlying dentin was also demonstrated. On the basis of the present results, the concept of prebonding rapid intrafibrillar mineralization was proposed. This user-friendly scheme introduced PAA-ACF-based intrafibrillar mineralization into dentin bonding for the first time. As multifunctional primers, PAA-ACF precursors have the potential to shed new light on prolonging the service life of adhesive restorations, with promising significance.

Automated summary

A prebonding rapid intrafibrillar mineralization strategy was developed to optimize dentin bonding durability. Polyacrylic acid-stabilized amorphous calcium fluoride (PAA-ACF) was used to induce rapid intrafibrillar mineralization of collagen, strengthen dentin mechanical properties, inhibit degradation and bacterial erosion, and demonstrate high-quality integration of the hybrid layer and dentin.