High-pressure torsion; Nanocomposites; Fragmentation; Process monitoring
A bulk nanocomposite with a FeTi-Cu composition was prepared using high-pressure torsion, and satisfactory microstructural homogeneity was achieved at high temperatures due to self-reinforcement. However, processing at room temperature remained challenging.
In order to develop materials for energy storage, a bulk nanocomposite with a composition of FeTi-25 vol% Cu was prepared by high-pressure torsion, with FeTi as functional phase for hydrogen storage and Cu as ductile phase to improve the processability. Despite the use of such a highly ductile auxiliary phase, the processability remained challenging due to strain localization in the softer Cu. This behavior is most pronounced at room temperature, and no nanocomposites were formed. At elevated temperatures, the strong strain rate sensitivity of the flow stress of the nanocrystalline Cu facilitates the formation of a FeTi-Cu nanocomposite due to a self-reinforcing process. Nevertheless, fragmentation of FeTi is limited because the resulting massive strain hardening prevents controlled processing at temperatures <250 degrees C, and Cu-rich shear bands develop at temperatures >250 degrees C. Satisfactory microstructural homogeneity is only achieved at the highest deformation temperatures of 550 degrees C. Overall, this study highlights that for unlikely material pairings, as often required in the pursuit of superior functional materials, the mechanical behavior of the phases involved and their interplay remains critical and must be thoroughly investigated when aiming for controlled structural homogeneity of bulk nanomaterials.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据