In this study, cellulose was extracted from honey pomelo peel using the compound enzyme method, and cellulose nanofibers (CNFs) were prepared from it. The optimized extraction scheme yielded a cellulose extraction yield of 36.57%. The CNFs had small average diameter and negative Zeta potential, as well as high crystallinity and specific surface area.
In this study, cellulose was extracted from honey pomelo peel (HPP) using the compound enzyme method and the cellulose nanofibers (CNFs) were prepared from it. The result of optimization experiment showed that the optimal extraction yield of cellulose was 36.57%. The optimal extraction scheme for cellulose was as follows: fixed pH at 4.8, temperature at 48 degrees C, extraction time of 75 min, and supplemental amount of HPP powder, pectinase, hemicellulase and laccase were 10, 0.10, 0.10, 0.20 g, respectively. The cellulose samples extracted and purified from HPP contained 74.73% holocellulose, 64.98% cellulose, 59.74% alpha-cellulose and 366 polymerization degrees. CNFs were prepared by hydrolyzing the moistened cellulose solution with 15 U/mL cellulase at 50 degrees C for 15 h, with the average diameter and Zeta potential of 68.15 nm and -24.1 mV. The crystallinity and specific surface area of CNFs were 60.12% and 193.87 m2/g, while the hydrostatic contact angle of CNFs increased with the ultrasound time. Thermogravimetric analysis showed that both the purified cellulose and CNFs had better thermal stability. Purified cellulose and CNFs play important roles in various fields such as food, medicine, and industry.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据