DOI: 10.1016/j.fuel.2023.130004
关键词
Maceral; Coal-based graphene; Yield; XRD; TEM
Graphene with stable structure and good extensibility can be prepared using the improved Hummers redox method. Different coal-based graphenes have different crystal characteristics, and the structural order and graphitization degree are related to coal rank and coal macerals.
Graphene is prepared using the improved Hummers redox method to study the preparation and structural characteristics of coal-based graphene from coal macerals of rank between 0.52 % and 1.98 %. The macerals are separated and enriched by hand sorting, sieving, and isopyknic gradient centrifugation. The crystal characteristics of the macerals, coal-based graphite, and graphene are characterized by XRD, Raman, SEM and TEM. The flake graphene with stable structure, good extensibility, different cell parameters and defects can be prepared from macerals. All the preparation yields are less than 4.0 %. The XRD data shows that after high-temperature graphitization, the layer spacing d(002) of each sample is less than 0.3400 nm, and the lamellar crystallite sizes L-a and L-c are 7.70-21.09 nm and 11.53-16.94 nm, respectively. After the redox reaction, inertinite MLI-GS, YCWI-GS, and vitrinite GMDV-GS have the layer spacing d(002), lamellar extendability L-a, stacking thickness L-c, and average stacking layer N-ave that tend to be graphite-like structure. The microcrystalline structure is well developed and stable. Raman also confirmes that inertinite and high-rank vitrinite-derived graphene have fewer structural defects, good ordering, and a high degree of graphitization. The average values of I-D/I-G and A(D)/A(G) of maceral -> coal-based graphite -> graphene are 0.73 -> 0.29 -> 1.06, 2.12 -> 0.40 -> 1.62, indicating a relationship between the structural order: coal-based graphite > maceral > graphene, and between the degree of graphitization: coal-based graphite > graphene > maceral. The SEM and TEM dates show that inertinite tends to form a flat graphene structure with four-six layers, and has good light transmission. The graphene has few folds and warps, good layer extensibility, and high lattice order. The layer spacing at the edge is consistent with the d(002) of XRD analysis. Vitrinite, cutinite, and barkinite derived graphene are similar to a kneaded paper balls. The layers are mixed with each other, forming more folds and ripples, and the peeling effect is poor. Only the high-rank GMDV-GS is clean like gauzy graphene, indicating that the micromorphological characteristics of graphene are related to the coal rank and macerals.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据