Zero-Dimensional Hybrid Antimony Chloride with Near-Unity Broad-Band Orange-Red Emission toward Solid-State Lighting

Zero-dimensional (0D) hybrid metal halides are attractive owing to their distinctive structure as well as photoluminescence (PL) characteristics. To discover 0D hybrid metal halides with high photoluminescence quantum yield and good stability is of great significance for white light-emitting diodes (LEDs). Herein, a novel hybrid antimony chloride (CTP)(2)SbCl5 is synthesized, which shows a bright broad-band orange-red emission peaking at 620 nm under the low energy excitation (365 nm), achieving an excellent photoluminescence quantum yield of 96.8%. In addition, (CTP)(2)SbCl5 shows an additional emission peaking at 470 nm when excited at high energy (323 nm). PL spectra and density functional theory results demonstrate that the observed dual-band emission originates from the singlet and triplet self-trapped excitons confined in isolated [SbCl5](2-) square pyramids. Moreover, (CTP)(2)SbCl5 presents relatively superior air stability, and the PL intensity still maintains 78% of the initial PL intensity when exposed to the air for above 2 weeks. Benefiting from high-efficiency PL emission and good stability of (CTP)(2)SbCl5, a stable warm white LED device with a 92.3% color rendering index was prepared by coating blue phosphor BaMgAl10O17:Eu2+, green (Sr,Ba)(2)SiO4:Eu2+, and orange-red (CTP)(2)SbCl5 on a 365 nm LED chip. This work provides an efficient luminescent material and also demonstrates the potential application of 0D hybrid antimony chloride in solid-state lighting.

Automated summary

A novel hybrid antimony chloride (CTP)(2)SbCl5 is synthesized, which exhibits high photoluminescence quantum yield and good stability. The material demonstrates dual-band emission and can be used for white light-emitting diodes (LEDs) with high color rendering index.