Bonding Strength of Various Luting Agents between Zirconium Dioxide Crowns and Titanium Bonding Bases after Long-Term Artificial Chewing

期刊

MATERIALS
卷 16, 期 23, 页码 -

出版社

MDPI
DOI: 10.3390/ma16237314

关键词

implant-abutment connection; hybrid abutment crown; adhesive cement; zirconium dioxide; bonding strength

向作者/读者索取更多资源

This study evaluated the effects of different luting agents on the bonding between zirconium dioxide crowns and titanium bonding bases. The results showed that most luting agents were suitable for cementation of zirconium dioxide crowns, meeting the recommended debonding force value.
The use of hybrid abutment crowns bonded extraorally to a titanium bonding base has aesthetic and biological benefits for the prosthetic rehabilitation of oral implants. The objective of this study was to evaluate the effects of luting agents between a zirconium dioxide crown and the titanium bonding base on crown/abutment retention and the subsequent durability of the prosthetic superstructure. Fifty-six implant abutment samples, all restored with a lower first premolar zirconium dioxide crown, were used and divided into seven groups (n = 8/group) according to the type of luting agent used: group 1, SpeedCEM Plus; group 2, Panavia SA Cement Universal; group 3, Panavia V5; group 4, RelyX Unicem 2 Automix; group 5, VITA ADIVA IA-Cem; group 6, Ketac CEM; and group 7, Hoffmann's Phosphate Cement. All specimens were subjected to thermomechanical loading (load of 49 N, 5 million chewing cycles and 54.825 thermocycles in water with temperatures of 5 degrees C and 55 degrees C). The surviving samples were exposed to a pull-off force until crown debonding from the bonding base. Overall, 55 samples survived the thermomechanical load. Group 2 showed the highest mean pull-off force value (762 N), whereas group 6 showed the lowest mean value (55 N). The differences between the seven groups were statistically significant (ANOVA, p < 0.001). The debonding failure pattern was mainly adhesive and was noticed predominantly at the zirconium dioxide-luting agent interface. Within the scope of the present investigation, it was shown that most of the luting agents are suitable for cementation of a zirconium dioxide crown onto a titanium base since the debonding forces are above a recommended value (159 N).

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.6
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据