Crystallographic texture and grain boundary character development of hot-press sintered tungsten heavy alloy: The effect of rhenium concentration

In this study, the effects of rhenium on the evolution of microstructure and texture in hot press sintered tungsten heavy alloy (93W-4.9Ni-2.1Cu) is examined. Rhenium is added (i.e., increased rhenium from 0 to 1 wt % with interval of 0.25 wt %) to a conventional tungsten heavy alloy while maintaining a constant Ni: Cu (7:3) ratio. The samples were prepared using a vacuum hot press sintering method with parameters including 50 MPa pressure, 10 degrees C/min heating rate, and 1450 degrees C temperature for a 20-min holding time. The impact of rhenium on densification, crystallographic texture development, and grain boundary features of Re alloyed WHA was studied using electron backscattered diffraction (EBSD). The development of grain boundary texture was the result of a Sigma 3 CSL increase in sintered compact. The base alloy exhibits fibre texture in the (001) plane with the <111> direction and a higher proportion of low-angle grain boundaries. Reduced kinetics of grain growth during sintering led to a higher degree of densification and randomised weak fibre texture in rhenium-alloyed samples. The deterioration of texture in the (001) <111> direction in rhenium-added alloys was caused by recrystallization following recovery during sintering. Metallographic studies reveal that an increase in rhenium in the WHA's stoichiometry resulted in particle refinement during sintering, thereby enhancing the WHA's properties. Maximum micro-hardness (432 HV0.5), electrical conductivity (23.74 % of IACS), and relative density (99.90 %) were observed in a 93W-4.9Ni-2.1Cu (Re 1 wt% alloy).

Automated summary

This study examines the effects of rhenium on the microstructure and texture evolution in hot press sintered tungsten heavy alloy (93W-4.9Ni-2.1Cu). The results show that adding rhenium can enhance the densification of the alloy, induce randomization of grain orientation, and improve the properties of the alloy.