Breakthrough curve analysis of phosphorylated hazelnut shell waste in column operation for continuous harvesting of lithium from water

In batch-scale operations, biosorption employing phosphorylated hazelnut shell waste (FHS) revealed excellent lithium removal and recovery efficiency. Scaling up and implementing packed bed column systems necessitates further design and performance optimization. Lithium biosorption via FHS was investigated utilizing a continuous-flow packed-bed column operated under various flow rates and bed heights to remove Li to ultra-low levels and recover it. The Li biosorption capacity of the FHS column was unaffected by the bed height, however, when the flow rate was increased, the capacity of the FHS column decreased. The breakthrough time, exhaustion time, and uptake capacity of the column bed increased with increasing column bed height, whereas they decreased with increasing influent flow rate. At flow rates of 0.25, 0.5, and 1.0 mL/min, bed volumes (BVs, mL solution/mL biosorbent) at the breakthrough point were found to be 477, 369, and 347, respectively, with the required BVs for total saturation point of 941, 911, and 829, while the total capacity was calculated as 22.29, 20.07, and 17.69 mg Li/g sorbent. In the 1.0, 1.5, and 2.0 cm height columns filled with FHS, the breakthrough times were 282, 366, and 433 min, respectively, whereas the periods required for saturation were 781, 897, and 1033 min. The three conventional breakthrough models of the Thomas, Yoon-Nelson, and Modified Dose-Response (MDR) were used to properly estimate the whole breakthrough behavior of the FHS column and the characteristic model parameters. Li's extremely favorable separation utilizing FHS was evidenced by the steep S-shape of the breakthrough curves for both parameters flow rate and bed height. The reusability of FHS was demonstrated by operating the packed bed column in multi-cycle mode, with no appreciable loss in column performance.

Automated summary

Biosorption using phosphorylated hazelnut shell waste (FHS) is a promising method for lithium removal and recovery. This study investigated the performance of a continuous-flow packed-bed column system using FHS for ultra-low level lithium removal. The results showed that the lihium biosorption capacity of the FHS column was unaffected by the bed height, but decreased with increasing flow rate.