关键词
PEDOT:PSS-based ternary electrode; Electrochemical performance; Specific capacitance; Reduced graphene oxide; supercapacitors
This study describes the synthesis and characterization of a ternary nanocomposite electrode for supercapacitors. The electrode, made of tin oxide/reduced graphene oxide wrapped with poly (3,4-ethylenedioxythiophene)-poly-(styrenesulfonate), exhibits excellent electrochemical properties and high cycling stability.
This study describes a ternary poly (3,4-ethylenedioxythiophene)-poly-(styrenesulfonate) (PEDOT:PSS)-wrapped tin oxide/reduced graphene oxide (SnO2/RGO/PEDOT: PSS) (SGP) nanocomposite electrode as a supercapacitor electrode. The properties of the SGP nanocomposites were studied using various characterization techniques such as X-ray Diffraction, scanning electron microscopy, energy-dispersive X-ray spectroscopy, transmission electron microscopy (TEM), Raman spectroscopy, and electrochemical impedance spectroscopy. The XRD results demonstrated the reduction of graphene oxide during the synthesis. TEM analysis confirmed the presence of PEDOT: PSS and graphene layers adorned with minuscule SnO2 particles. Standard three-electrode geometry was used to investigate the electrochemical properties of the samples. For comparison, a two-electrode system was used to investigate the electrochemical properties. The as-prepared SGP nanocomposite electrode exhibited specific capacitance of 252.0 F/g and 124 F/g at a scan rate of 1 mV/s for the three-electrode and two-electrode systems, respectively. Furthermore, the electrode retained approximately 97.8 % of its capacitance even after 5000 cycles. However, the SGP electrode when operated to wide voltage window -0.6 V to +0.6 V exhibited the maximum specific capacitance of 285.0 F/g at scan rate 1 mV/sec and shows 114 % enhancement in the capacitance retention after the 5000 cycles at current density of 10 A/g which gives a protocol for future energy storage device application with high operating voltage. The SGP-based supercapacitor exhibited a high energy density (17.7 Wh kg (-1)) and power density (1220 W kg (-1)).
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据