SURFACE & COATINGS TECHNOLOGY
卷 476, 期 -, 页码 -出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.surfcoat.2023.130251
关键词
PEO; Ta-12W alloy; Microstructure evolution; Ultra-low porosity; Gas bubble
This study focuses on the modification of PEO coatings on Ta-12W alloy using NH4F additive. The results show that ultra-low porosity coatings can be prepared by optimizing the NH4F content. The formation process of specific structures on the coating surface is discussed, and the effects of NH4F concentration and treatment duration on coating characteristics are investigated.
The sealing of pores in plasma electrolytic oxidation (PEO) coatings is critical to further enhance the protection of the underlying substrate and maintain the mechanical performance of coatings. This study focuses on the modification of the surface microstructure of PEO coatings on Ta-12W alloy by introducing NH4F additive into a mixed silicate-phosphate electrolyte. As a result, ultra-low porosity coating with a surface porosity of less than 1 % is effectively prepared. Detailed investigations have been conducted to study the effects of NH4F content and treatment duration on various coating characteristics, including microscopic morphology, elemental distribution, thickness, and phase composition. It is found that optimizing the concentration of NH4F eliminates the large pore structures and promotes the development of Ta-rich structures resembling pancakes on the coating surface. Furthermore, the intensities of diffraction peaks from different crystal faces of Ta2O5 in coatings exhibit variations, and selective growth is observed specifically on its (110) crystal plane. After a 20-minute treatment of Ta12W alloys in the electrolyte containing 4 g/L NH4F, the surface of the coating displays predominantly pancakelike structures with sealed pore/non-pore features. The formation process of these specific structures is discussed based on the evolution of coating morphology with oxidation time. It is proposed that the increase in anodic voltage and gas production in the late stage favors the breakdown of gas bubbles, leading to the creation of nonporous pancake-like structures on the surface. In addition, the breakdown of the dielectric layer at the periphery of gas bubbles results in the influx of film-forming materials into pores, which causes the formation of pancakelike structures with sealed pores.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据