Chitosan-grafted hydrogels for heavy metal ion adsorption and catalytic reduction of nitroaromatic pollutants and dyes

Chitosan-grafted-poly(acrylic acid) (CS-g-PAA) and chitosan-grafted- poly(2-acrylamido-2-methyl-1-propanesulfonic acid) (CS-g-P(AA-co-AMPS)) hydrogels were synthesized and then employed as adsorbents for the effective removal of Cu2+ and other heavy metal ions. The effect of hydrogel's composition on the Cu2+ adsorption was explored. The CS-g-PAA hydrogel demonstrated a superior adsorption capacity compared to pristine CS, PAA hydrogel, and CS-g-P(AA-co-AMPS) hydrogels. The adsorption followed the Langmuir isotherm model, and the pseudo-second order kinetic model. Additionally, the CS-g-PAA hydrogel exhibited relatively high adsorption performances toward Cr3+, Co2+, Ni2+, Pb2+, and Zn2+. Metal ions adsorbed within CS-g-PAA hydrogels underwent reduction to their corresponding metallic states and were reutilized as catalysts for the reduction of 4-nitrophenol. The comparative catalytic performances of the metal species in the hydrogel were in the order of Cu > Ni > Co > Zn. The reduction efficiency of Cu-CS-g-PAA increased with increased catalyst dosage, NaBH4 concentration, and temperature. A very low activation energy of 3.7 kJ/mol was observed. The catalyst maintained high catalytic performance even when subjected to real water samples and proved its reusability for up to three cycles. Moreover, the catalyst could effectively reduce 2-nitrophenol and methyl orange.

Automated summary

Chitosan-grafted-poly(acrylic acid) and chitosan-grafted-poly(2-acrylamido-2-methyl-1-propanesulfonic acid) hydrogels have shown effective adsorption properties for Cu2+ and other heavy metal ions, and can also act as catalysts for reduction reactions.