Cyclic fatigue; Nickel-titanium alloy; 2Shape; Heat-treatments; Temperature; CM-wire
The objective of this study was to evaluate the influence of different heat treatments and temperatures on the cyclic fatigue resistance of 2Shape instruments. The results showed that CM-Wire instruments exhibited the highest cyclic fatigue resistance. Body temperature negatively affected the cyclic fatigue resistance of certain instruments compared with room temperature.
Objectives To evaluate the influence of different heat treatments and temperatures on the cyclic fatigue resistance of 2Shape instruments (Micro Mega, Besancon, France) with the same design. Materials and methods A total of 80 2Shape TS1 (#25/.04) and 80 TS2 (#25/.06) files with different heat treatments (no heat-treated, NHT; C-Wire; T-Wire; CM-Wire) were tested at room (25 +/- 1 ?) and body (37 +/- 1 &?) temperatures in 16-mm stainless steel artificial canal with a curvature of 60 and 5 mm of radius. Files were tested in continuous rotation at 300 rpm using a customized device. Cyclic fatigue resistance was expressed in the number of cyclic to fracture (NCF). The phase transformation temperature of each file was determined by differential scanning calorimetry. Data were statistically analyzed using the two-way ANOVA and the Bonferroni post-hoc test with p < 0.05. Results All CM-Wire TS1 and TS2 files showed higher NCF than the other groups at both temperatures (p < 0.001). C-Wire TS2 showed higher resistance than NHT and T-Wire TS2 (p < 0.001), with no significant differences between the last two. Body temperature significantly decreased NCF of all tested files (p < 0.05) except for NHT and T-Wire TS1. Conclusions Body temperature negatively affected the cyclic fatigue resistance of C-Wire and CM-Wire TS1 and of all TS2 files compared with room temperature. The CM-Wire instruments exhibited the highest cyclic fatigue resistance of all tested files.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据