Characteristic analysis of s-Fe/Cu two-component micro-electrolysis materials and degradation of dye wastewater

期刊

ENVIRONMENTAL SCIENCE AND POLLUTION RESEARCH
卷 30, 期 16, 页码 46574-46586

出版社

SPRINGER HEIDELBERG
DOI: 10.1007/s11356-023-25477-9

关键词

s-Fe/Cu bimetal; Micro-electrolysis; Catalysis; Dye; Degradation mechanism; Sponge iron

向作者/读者索取更多资源

Micro-electrolysis is a pretreatment technology for difficult-to-biodegrade wastewater. In this study, a chemical displacement method was used to load copper on the surface of sponge iron (s-Fe), and then it was mixed with activated carbon and other components to obtain a multi-element micro-electrolytic filler (OMEF). The results showed that OMEF had a specific surface area of 88.374 m(2)/g, various functional groups, active materials, and a better performance in terms of COD removal compared to commercial fillers.
Micro-electrolysis is a pretreatment technology for difficult-to-biodegrade wastewater. In this study, a chemical displacement method was used to load copper on the surface of sponge iron (s-Fe), and then it was mixed with activated carbon and other components to obtain a multi-element micro-electrolytic filler (OMEF). Through BET, SEM, XRD, XPS, and FT-IR characterization and analysis, OMEF was proved to have a specific surface area of 88.374 m(2)/g, C-C, C-O, C = O, O-C = O, and other functional groups and Fe3C, MnO2 and other active materials. The removal mechanism of organic pollutants in wastewater by OMEF could be due to the galvanic reaction, direct reduction of Fe, oxidation of Fe, catalytic oxidation of Cu and Mn, and co-precipitation of adsorption. The coupling of the micro-electrolysis and biological methods proved that OMEF had excellent application efficiency. The results indicated that the COD removal rates of OMEF and commercial fillers reached 88.39% and 48.02%, respectively, and the B/C reached 0.74 and 0.3. OMEF showed a better performance. The reusability of the OMEF filler was measured to ensure that the B/C was maintained at around 0.5 during 5 cycles. Kinetic analysis showed that the degradation data of methyl orange (MO) and the removal data of COD obeyed pseudo-second-order kinetics. Moreover, it can further broaden the pH range of treated wastewater and increase the oxidation rate. This new strategy has brought potential enlightenment for the development of high-efficiency wastewater pretreatment using new micro-electrolysis materials. The excellent performance of OMEF micro-electrolytic filler in pretreatment indicated its potential for industrial application.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.7
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据