CHEMICAL ENGINEERING JOURNAL
卷 451, 期 -, 页码 -出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.cej.2022.139074
关键词
Methane conversion; Rh single atom; Cu single atom; Al2O3 nanoparticles; Acetic acid; Ethanol
Efficient and selective electro-conversion of methane to C2 compounds (acetic acid and ethanol) at ambient temperature was achieved using enhanced catalysts with tunable electrocatalytic activities. Rh-based electrocatalyst showed high acetic acid production rate after only 40 minutes of reaction, while Cu-based catalyst achieved high selective ethanol production rate after 120 minutes of reaction. The catalysts remained stable for at least 120 minutes at 2 V and ambient temperature, and showed high efficiency and stability compared to literature results.
The production of C2 compounds in an aqueous solution by efficient and selective electro-conversion of methane is a challenge and of great significance topic. Here, enhanced catalysts, with tunable electrocatalytic activities with time, for direct and selective oxidation of methane to C2 products (i.e., acetic acid and ethanol) at ambient temperature were prepared by exploiting Rh and Cu single atoms dispersed on NH4BF4 modified Al2O3 nanoparticles exhibiting a large amount of Br circle divide nsted acid sites. Bronsted acid sites play a pivotal role in the final formation allowing the direct CO insertion into reaction intermediates. A high acetic acid production, over the Rh-based electrocatalyst, of 33.57 mu mol/hcm(2) after only 40 min of reaction was obtained. On the other hand, a selective ethanol production rate of 37.14 mu mol/hcm(2) after 120 min of reaction was achieved over the Cu-based catalyst, thanks to the tendency vs acetyl species formation over copper single atoms. Catalysts activity was kept stable for at least 120 min, at 2 V, and ambient temperature. The comparative analysis with the literature results highlights the high efficiency of our catalysts in selectively promoting acetic acid and ethanol productions with high yields, and stability. A novel way, exploiting single-atoms dispersed on suitable supports, for the production of performing surfaces, was provided.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据