期刊
DALTON TRANSACTIONS
卷 52, 期 21, 页码 7208-7218出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/d3dt01106b
关键词
-
The rational design and controllable synthesis of high-performance energy storage materials are important measures to address the growing demand for energy storage devices. This work involves the growth of a fishnet-like Fe2O3 nanorod@oxygen-rich carbon layer structure directly onto carbon fiber cloth as a binder-free electrode for symmetric capacitors.
The rational design and controllable synthesis of high-performance energy storage materials are important measures to address the growing demand for energy storage devices. This work involves the growth of a fishnet-like Fe2O3 nanorod@oxygen-rich carbon layer structure directly onto carbon fiber cloth as a binder-free electrode for symmetric capacitors. The growth of Fe2O3 nanorods provided a large specific surface area, and the coating of an oxygen-rich carbon layer protected the Fe2O3 nanorods as an active substance. Furthermore, oxidation treatment created rich electrochemically active sites by loading oxygen-containing functional groups onto the composite surface. As a result, the optimal OC@Fe2O3-ACC sample exhibited a high areal specific capacitance of 1687 mF cm(-2) at a current density of 1 mA cm(-2). Meanwhile, an excellent capacity retention rate of 58.7% was achieved at 15 mA cm(-2). Finally, the long-term cycling stability was verified with an 80% retention rate of the initial capacitance after 12 000 cycles.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据