INFLUENCE OF THE SPEED OF DOWNWARD SEMI-CONTINUOUS CASTING ON THE CRYSTAL SIZE AND MECHANICAL PROPERTIES OF RECYCLED COPPER

In this study, the influence of the speed of downward semi-continuous casting on the crystal size and mechanical properties of recycled copper after casting and cold deformation was investigated. It was shown that the increase in the casting speed from 0,09 m / min to 0,22 m / min resulted in refinement of the macrostructure and reduction of the crystal cross-sectional area from 3,221 mm2 to 1,2 mm2, which resulted in an increase in microhardness after casting by 8 %, while in the state after cold working, an increase in microhardness by 3 % and ultimate tensile strength by 2,5 %.

Automated summary

The influence of the speed of downward semi-continuous casting on the crystal size and mechanical properties of recycled copper after casting and cold deformation was investigated. It was found that increasing the casting speed resulted in refined macrostructure, reduced crystal cross-sectional area, and increased microhardness and ultimate tensile strength.