4.6 Article

A nanoscale inorganic coating strategy for stabilizing hydrogel neural probes in vivo

期刊

JOURNAL OF MATERIALS CHEMISTRY B
卷 -, 期 -, 页码 -

出版社

ROYAL SOC CHEMISTRY
DOI: 10.1039/d3tb00710c

关键词

-

向作者/读者索取更多资源

This study aims to improve the stability of chemically cross-linked poly(vinyl alcohol) (PVA) hydrogel fibers by using atomic layer deposition (ALD) to coat them with an inorganic silicon dioxide (SiO2) layer. SiO2-coated PVA hydrogel fibers showed superior stability and preserved their mechanical and optical properties compared to uncoated fibers. In vivo experiments demonstrated that these SiO2-coated PVA hydrogel fibers could be used to optically activate the motor cortex and modulate locomotor behaviors in transgenic mice.
Hydrogels with adaptable optical and mechanical characteristics show considerable promise for light delivery in vivo with neuroengineering applications. However, the unlinked amorphous polymer chains within hydrogels can cause volumetric swelling after water absorption under physiological conditions over time. Chemically cross-linked poly(vinyl alcohol) (PVA) hydrogels showcase fatigue-resistant attributes and promising biocompatibility for the manufacture of soft neural probes. However, possible swelling of the PVA hydrogel matrix could impact the structural stability of hydrogel-based bioelectronics and their long-term in vivo functionality. In this study, we utilized an atomic layer deposition (ALD) technique to generate an inorganic, silicon dioxide (SiO2) coating layer on chemically cross-linked PVA hydrogel fibers. To evaluate the stability of SiO2-coated PVA hydrogel fibers mimicking the in vivo environment, we conducted accelerated stability tests. SiO2-coated PVA hydrogel fibers showed improved stability over a one-week incubation period under a harsh environment, preventing swelling and preserving their mechanical and optical properties compared to uncoated fibers. These SiO2-coated PVA hydrogel fibers demonstrated nanoscale polymeric crystalline domains (6.5 & PLUSMN; 0.1 nm), an elastic modulus of 73.7 & PLUSMN; 31.7 MPa, a maximum elongation of 113.6 & PLUSMN; 24.2%, and minimal light transmission loss (1.9 & PLUSMN; 0.2 dB cm(-1)). Lastly, we applied these SiO2-coated PVA hydrogel fibers in vivo to optically activate the motor cortex of transgenic Thy1::ChR2 mice during locomotor behavioral tests. This mouse cohort was genetically modified to express the light-sensitive ion channel, channelrhodopsin-2 (ChR2), and implanted with hydrogel fibers to deliver light to the motor cortex area (M2). Light stimulation via hydrogel fibers resulted in optogenetically modulated mouse locomotor behaviors, including increased contralateral rotation, mobility speeds, and travel distances.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.6
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据