关键词
DC magnetron sputtering; Coating modification; Compositing types; Corrosion resistance; Antibacterial activity; Cytocompatibility
In order to improve the corrosion resistance, antimicrobial efficacy, and cytocompatibility of titanium-based implants, multifunctional coatings based on CuO and ZnO in the forms of mono, double, and co-existence were designed by adjusting the sputtering orders under magnetron sputtering. The coatings exhibited improved surface roughness, reduced contact angle, increased corrosion potential, and enhanced bactericidal properties. Moreover, the coatings supported cell viability and proliferation due to their strong metal-oxygen bonding and rough surface. The double layered coating with ZnO as the bottom layer and CuO as the upper layer showed the best overall properties.
To obtain an overall enhancement on corrosion resistance, antimicrobial efficacies, and cytocompatibility of titanium-based implants, the multifunctional coatings in the forms of mono, double, and co-existence based on CuO and ZnO were innovatively designed by regulating the sputtering orders under magnetron sputtering. The results showed that ZnO and CuO were pure phases, CuO grains performed large and unevenly while ZnO grains were fine and homogeneous, such grains morphology features remerged on double-layered coatings. The surface roughness (Rq) of the monolayer to the double layer and then to the co-existing one was increased from 2.58 nm to 18 nm to 22.6 nm. All multifunctional coatings helped to lower the contact angle to a minimum of 18.82 degrees, and enhanced the corrosion potential to a maximum of-0.261 V. The released ions, grains piercing, and ROS produced by p-n junctions co-played the bactericidal roles, which equipped ZnO/CuO composite coatings with bactericidal rates of 90.24%-100% as directly contact with the target germs in 0.5 h. Owing to the strong metal-oxygen bonding and rough surface, all coatings supported the cell viabilities of 137.92%-145.27% through 120 h co-culturing, MC3T3-E1 cells healthily proliferated and adhered on the surface. The double layered coating, with ZnO as the bottom layer and CuO as the upper layer, exhibited better overall properties.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据