期刊
MATERIALS LETTERS
卷 352, 期 -, 页码 -出版社
ELSEVIER
DOI: 10.1016/j.matlet.2023.135129
关键词
Metals and alloys; Microstructure; Mechanical properties; Stacking faults; Fracture
The effect of Ti and Sr on the microstructure and mechanical properties of Al-Si-Cu-Ni alloy was investigated. It was found that the addition of 0.1% Ti and 0.02% Sr led to a significant reduction in grain size and a change in the morphology of eutectic Si. Sr promoted the formation of stacking faults and nano-Al2Cu. The ultimate tensile strength, yield strength, and elongation were greatly increased, reaching 239.6 MPa, 140.6 MPa, and 2.11% respectively.
The effect of Ti and Sr on the microstructure and mechanical properties of Al-Si-Cu-Ni alloy was studied. Research showd that the addition of 0.1% Ti and 0.02% Sr significantly reduced grain size and changed the morphology of eutectic Si. Sr promoted the formation of stacking faults and nano-Al2Cu. The strength and plasticity were significantly increased with ultimate tensile strength, yield strength and elongation being 239.6 MPa, 140.6 MPa, and 2.11%, respectively.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据