We synthesize a new vanadium oxyfluoride VO2F (rhombohedral, R3c) through a simple one-step ball-milling route and demonstrate its promising lithium storage properties with a high theoretical capacity of 526 mA h g(-1). Similar to V2O5, VO2F transfers into an active disordered rock-salt (Fm3m) phase after initial cycling against the lithium anode, as confirmed by diffraction and spectroscopic experiments. The newly formed nanosized LixVO2F remains its crystal structure over further cycling between 4.1 and 1.3 V. A high capacity of 350 mA h g(-1) at 2.5 V was observed at 25 degrees C and 50 mA g(-1). Furthermore, superior performance was observed for VO2F in comparison with a commercial crystalline V2O5, in terms of discharge voltage, voltage hysteresis and reversible capacity.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据