CLINICAL ORAL INVESTIGATIONS
卷 20, 期 6, 页码 1175-1179出版社
SPRINGER HEIDELBERG
DOI: 10.1007/s00784-015-1611-4
关键词
Cyclic fatigue; Retreatment; Rotary instrument; Sodium hypochlorite
The aim of this study was to investigate the effect of immersion in sodium hypochlorite (NaOCl) on cyclic fatigue resistance of three different rotary nickel-titanium (NiTi) retreatment files. A total of 90 new ProTaper, D-RaCe, and Mtwo retreatment files were tested. Thirty files of the same brand were randomly assigned to two groups (n = 15). Group 1 was no immersion (control group) and 16 mm of group 2 instruments were immersed in 5 % NaOCl at 37 A degrees C for 5 min. All instruments were then tested for cyclic fatigue. Resistance to cyclic fatigue was determined by counting the numbers of cycles to failure in a 60A degrees curve with a 5-mm radius, recording the time in seconds to fracture. Data were analyzed by two-way analysis of variance. Resistance to cyclic fatigue decreased significantly for D-RaCe retreatment files after immersion in NaOCl. ProTaper and Mtwo retreatment files were not affected from immersion to NaOCl. D-RaCe retreatment instruments showed better cyclic fatigue resistance than ProTaper and Mtwo retreatment instruments, and the difference was statistically significant (p < 0.05). There was no significant difference between ProTaper and Mtwo retreatment instrument groups (p > 0.05). D-RaCe retreatment instruments had the highest cyclic fatigue resistance among retreatment files tested in this study, but immersion to NaOCl decreased the cyclic fatigue resistance of D-RaCe retreatment instrument. It should be considered that cyclic fatigue resistance of D-RaCe can decrease in contact with NaOCl during the removal of canal filling material.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据