The composition-dependent structural and electrical properties of SnOx films prepared by means of reactive DC sputtering at various oxygen partial pressures (PO) and post-heat treatment temperatures (T-A) were investigated, toward these films' potential use in p-channel oxide thin-film transistors (TFTs). A SnOx film fabricated under the lowest studied P-O of 4% and heat-treated at 210 degrees C consisted of dendritic phases and irregular protrusions of metallic Sn. The resulting p-channel SnOx thin-film transistors suffered from marginal field effect mobility (mu(FE)) and low on/off current ratio (I-ON/OFF), suggesting that the imperfect phases caused by oxygen-deficient stoichiometry hinder hole carrier conduction and act as bulk trap states. The heterogeneous structures observed in SnOx films annealed at 210 degrees C could be eliminated by increasing P-O during fabrication. The resulting TFTs based on p-type SnOx films prepared at the high P-O of 8% showed high mobilities up to 2.8 cm(2) V-1 s(-1) and reasonable I-ON/OFF of approximately 10(3), demonstrating the critical role of these films' homogeneous ordered aggregates without any imperfect phases such as a dendritic phase or irregular protrusions of metallic Sn. Among TFTs based on the films fabricated under 8% P-O, the mu(FE) and I-ON/OFF performance metrics degraded with increasing T-A from 210 to 300 degrees C, which was mainly related to the 2SnO -> SnO2 + Sn disproportionation reaction.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据