A controlled, template-free, and hydrothermal synthesis route to sphere-like α-Fe2O3 nanostructures for textile dye removal

Iron carbonate nanospheres were synthesized via hydrothermal treatment of aqueous solutions of iron sulfate, ascorbic acid and ammonium carbonate with a molar ratio of 1 : 1 : 3, respectively, at 140 degrees C for 1.5 h. Pure alpha-Fe2O3 nanoparticles with an average crystallite size of 10.5-32 nm were produced by thermal decomposition of FeCO3 at 400-600 degrees C for 2 h. The compositions of the products were identified by means of XRD, FE-SEM, HR-TEM, FT-IR, BET, zeta potential and thermal analysis. The adsorption properties of alpha-Fe2O3 were evaluated using reactive red 195 (RR195) dye. Various parameters influencing the adsorption process were investigated, using a batch technique. The results show that alpha-Fe2O3 nanoparticles show good adsorption capacity and the dye removal percentage reaches about 98.77% in 10 min. Plus, increasing the surface area of the alpha-Fe2O3 nanoparticles from 107.7 to 165.6 m(2) g(-1) increases the adsorption capacity from 4.7 to 20.5 mg g(-1). Moreover, the adsorption data fit the Langmuir isotherm model well and the thermodynamic parameters exhibited an endothermic and spontaneous nature for the adsorption of RR195 dye on the hematite adsorbent.