Friction stir welding; Dissimilar T-joint; 2024 aluminum alloy; Copper; Mechanical properties; Metallurgical structure
In this research, T-joining of AA2024-T4 and commercially pure copper were performed successfully using friction stir welding. Effect of welding parameters on metallurgical and mechanical characteristics of the joints was studied. For this purpose, tensile strength, microhardness, and macro-and microstructures of the joints were investigated. Also, the fracture surfaces were examined using XRD and SEM. The best results were obtained for the 1130 rpm rotation speed (omega) and 12 mm/min travel speed (v), with the UTS of 156 MPa (similar to 70% of Cu strength). The microhardness test showed that TMAZ and base metal of Al side had the maximum hardness amounts (148 and 155 HV, respectively). Generally, increase in the omega(2)/v ratio caused the nugget zone and HAZ grain size to increase. The results revealed the formation of Al2Cu and Al4Cu9 intermetallic compounds in the border zone of the joints. The fractography results showed the occurrence of cleavage fracture in all the samples.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据