TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA
卷 26, 期 1, 页码 51-62出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/S1003-6326(16)64087-6
关键词
Al-Zn-Mg alloy; hot compression; dynamic phenomena; microstructure
资金
- Ministry of Education, China [20130161110007]
- Hunan Provincial Innovation Foundation for Postgraduate, China [CX2013B128]
- Chinese Scholarship Council [201306130021]
The AA7150 aluminum alloy was compressed to various strains at strain rate of 10 s(-1) and temperatures of 300 degrees C and 450 degrees C, respectively. Flow stress behavior, substructure evolution, morphology and spatial distribution of precipitates were studied based on differential scanning calorimetry analysis and transmission electron microscope observation. The results showed that dynamic flow softening occurs during hot deformation. The main softening mechanism could be concluded as dynamic recovery at 300 degrees C and continuous dynamic recrystallization at 450 degrees C. The clear heterogeneous spatial distributions of precipitates are found during deformation and enhanced with increased strain. Higher contents of Cu in T phases are found at 450 degrees C than at 300 degrees C, which present a transformation process from T phases to S phases as well. The associated evidence of dynamic precipitation on dislocations and particle-stimulated nucleation, as well as the detailed microstructural inherited relationship and morphological texture (particles preferred orientation) were characterized.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据