期刊
SYNTHETIC METALS
卷 220, 期 -, 页码 227-235出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.synthmet.2016.06.008
关键词
Three-dimensional graphene; Porous; Polyfurfuryl alcohol; Polyaniline; Composite material; Supercapacitor
资金
- Nanjing University of Posts and Telecommunications basic research program [NY 212002]
- Ministry of Education of China Innovative Research Team in University [IRT1148]
- Key Project of National High Technology Research of China [2011AA050526]
- Director Foundation of Xi'an Institute of Optics and Precision Mechanics [Y455A41ZZ0]
In this work, a 3D porous graphene (3DrGO) was prepared by a hydrothermal assembly process of graphene oxide (GO) using polyfurfuryl alcohol (PFA) spheres as the template followed by thermal reduction. The introduction of PFA spheres can effectively enlarge the interspace between graphene sheets and suppresses their re-stacking in the thermal treatment. The 3DrGO was further composted with PANI nanowire. The structure and the property of 3DrGO and 3DrGO/PANI composite have been characterized by transmission electron microscopy, scanning electron microscopy, X-ray photoelectron spectroscopy, Fourier transform infrared spectroscopy, X-ray diffraction, cyclic voltammetry, galvanostatic charge discharge test and electrochemical impedance spectroscopy. Electrochemical test reveals that the 3DrGO has good capacitance performance of 104 F/g at current charge-discharge current density of 1A/g and the capacitance performance increase to 530 F/g after further composed with PANI nanowire. Both 3DrGO and 3DrGO/PANI show excellent capacity retention rates of 95% and 88%, respectively, after 1000 cycles. All these impressive results demonstrate that the material obtained by this approach is greatly promising for application in high-performance supercapacitors. (C) 2016 Elsevier B.V. All rights reserved.