SURFACE AND INTERFACE ANALYSIS
卷 48, 期 12, 页码 1299-1304出版社
WILEY-BLACKWELL
DOI: 10.1002/sia.6036
关键词
6063 Al alloy; AlSiFe; anodic oxidation; extrusion; gloss
资金
- National Natural Science Foundation of China [51405328]
AlSiFe phase can form microscopic galvanic couples that decrease corrosion resistance of 6063 aluminum which may influence the anodizing process. Two samples of 6063 aluminum were prepared. One sample was cut along the extrusion direction of the billet, and the other was cut perpendicular to the extrusion direction. Both samples exhibited the same characteristics, except for the distribution of the second phase AlSiFe. Both samples were subjected to anodizing treatments. Comparison between anodic oxide films was performed. The microstructure of Al substrates and anodic oxide films were examined using a scanning electron microscope, an optical microscope, and a glow discharge optical emission spectrometer. Results indicated that the thicknesses and elemental distributions of the anodic oxide films were almost the same. Moreover, the second phase AlSiFe influenced the anodic oxidation process, resulting in cavities in the anodic oxide film that affected its brightness. Copyright (c) 2016 John Wiley & Sons, Ltd.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据