期刊
SURFACE & COATINGS TECHNOLOGY
卷 296, 期 -, 页码 185-191出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.surfcoat.2016.04.040
关键词
MoS2; Magnetron sputtering; Friction; Tribofilm
资金
- National Natural Science Foundation of China [51405477, 11475236]
In this paper, the composite Mo-S-N solid lubricant films are synthesized by magnetron sputtering of molybdenum disulphide (MoS2) target in nitrogen and argon atmosphere. With the increase of the nitrogen content, the nitrogen concentration in the deposited films increases from 0 to 35 at.%, and the corresponding S/Mo atomic ratio reduces to below 0.70. X-ray diffraction (XRD) and Raman spectroscopy analyses reveal that introducing nitrogen into films leads to the formation of amorphous structure and chemical bonds between nitrogen and molybdenum were detected by X-ray photoelectron spectroscopy. The hardness and elastic modulus of Mo-S-N films increase more than one order of magnitude higher than that of pure MoS2 films with increasing the N-2 flow rate (i.e., with increasing N content), reaching to the maximum of 9.59 and 113.12 GPa, respectively. The tribological properties of the prepared films tested by a ball-on-disc tribometer under a low-pressure vacuum exhibit that the incorporation of a suitable content of N dopant could significantly reduce the wear rate, however, both friction coefficient and wear rate increase dramatically in excess a certain amount of N dopant. (C) 2016 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据