SUPERLATTICES AND MICROSTRUCTURES
卷 89, 期 -, 页码 153-169出版社
ACADEMIC PRESS LTD- ELSEVIER SCIENCE LTD
DOI: 10.1016/j.spmi.2015.10.044
关键词
Chalcogenides; Thin films; Thermal evaporation deposition (PVD); Optical properties; Electrical properties
Compositional dependence of optical and electrical properties of chalcogenide CdSxSe1-x (0.4 >= x >= 0.0 at. %) thin films was studied. Cadmium sulphoselenide films were deposited by thermal evaporation technique at vacuum (8.2 x 10(-4) Pa) onto preheated glass substrates (523 K). The evaporation rate and film thickness were kept constant at 2.50 nm/s and 375 +/- 5 nm, respectively. X-ray diffractograms showed that, the deposited films have the low crystalline nature. Energy dispersive analysis by X-ray (EDAX) was used to check the compositional elements of deposited films. The absorption coefficient was determined from transmission and reflection measurements at room temperature in the wavelength range 300-2500 nm. Optical density, skin depth, optical energy gap and Urbach's parameters of CdSSe thin films have also been estimated. The direct optical energy gap decreased from 2248 eV to 1.749 eV when the ratio of Se-content was increased from 0.60 to 1.00. Conduction band and valance band positions were evaluated. The temperature dependence of dc-electrical resistivity in the temperature range (293-450 K) has been reported. Three conduction regions due to different conduction mechanisms were detected. Electrical sheet resistance, activation energy and pre-exponential parameters were discussed. The estimated values of optical and electrical parameters were strongly dependent upon the Se-content in CdSSe matrix. (C) 2015 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据