SOLAR ENERGY MATERIALS AND SOLAR CELLS
卷 158, 期 -, 页码 84-90出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.solmat.2016.05.041
关键词
Ion-implantation; Poly-silicon; Passivating contact; IBC c-Si solar cells
Ion-implanted poly-crystalline silicon (poly-Si), in combination with a tunnel oxide layer, is investigated as a carrier-selective passivating contact in c-Si solar cells based on an interdigitated back contact (IBC) architecture. The optimized poly-Si passivating contacts enable low interface recombination, resulting in implied V-OC (iV(OC)) of about 720 mV and 704 mV for n-type and p-type, respectively, before any hydrogenation step. It is found that high-quality passivation can be obtained when confining the dopants within the poly-Si layers and realizing a shallow diffusion of dopants into the c-Si bulk, meaning a sharp decrease in doping concentration in the c-Si at the poly-Si/c-Si interface. The doping profile at the polySi/c-Si interface can be influenced by poly-Si layer thickness, poly-Si ion-implantation parameters, and post-implantation annealing conditions. The detailed discussion on the passivation properties of the poly-Si passivating contacts and their preparation conditions are presented in this paper. In addition, IBC solar cells with/without front surface field (FSF) are fabricated, with the optimized poly-Si passivating contacts as back surface field, BSF (n-type poly-Si), and emitter (p-type poly-Si). The best cell shows an efficiency of 21.2% (V-OC=692 mV,J(SC)=39.2 mA/cm(2), FF=78.3%, and pFF=83.5%). (C) 2016 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据