期刊
SOFT MATTER
卷 12, 期 19, 页码 4443-4448出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/c6sm00286b
关键词
-
类别
资金
- National Research Foundation of Korea (NRF) - Korea Government (MEST) [2014R1A2A1A11052446]
- GIST Research Institute (GRI)
Conjugated-polymer nanofibers with a thermodynamically stable, coarsened, disordered structure in an amorphous glassy state were fabricated via a freeze-drying method using a poly(diphenylacetylene) derivative. The nanofibers were extremely emissive, with a fluorescence (FL) quantum yield of approximately 0.34, which was much higher than that of both the cast film (0.02) and the solution (0.21). Similarly, the amplitude-weighted average FL lifetime of the nanofibers was 0.74 ns, which was much longer than that of the film (0.29 ns) and the solution (0.57 ns). This unusual and enhanced FL-emission behavior was attributed to the abruptly quenched chain structure that was created by the freeze-drying process. The polymer chains in the nanofibers remained frozen-in and the side phenyl rings were retained in a relaxed state. The metastable chains did not undergo vibrational relaxation and collisional quenching to generate the radiative emission decay effectively.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据