SCIENCE AND TECHNOLOGY OF ADVANCED MATERIALS
卷 17, 期 1, 页码 71-79出版社
TAYLOR & FRANCIS LTD
DOI: 10.1080/14686996.2016.1152563
关键词
Coatings; wear; friction; self-lubrication; quasicrystals
资金
- Conselho Nacional de Pesquisa (CNPq), Brazil
- OGRAMAC Ltd (Santo Antonio da Posse/SP)
- CNPq
After gas atomization, a quasicrystalline powder based on aluminium was used to prepare a thick coating by high-velocity oxygen-fuel flame torch spraying. This layer was deposited on top of a bond-coat layer on a steel plate. A post-spraying annealing treatment turned the two layers to their stable state, a.-brass crystal and an icosahedral quasicrystal, respectively. The projection parameters were selected in such a way that the coating behaved like a self-lubricating material, which offered very good wear resistance (duration of pin-on-disk tests superior to 5 km with negligible material loss) and low friction (mu <= 6% against sintered tungsten carbide), in contrast to the state of the art. This property was achieved thanks to, on the one hand, excellent bonding to the substrate via the bound coat, and on the other hand, presence at the boundaries between quasicrystalline flakes of a mixture of both threefold and fourfold coordinated carbon originating from spray processing. Application to hard materials used in mechanical devices is appealing, especially because soft, lubricating additives may not be needed, thus considerably increasing the lifetime of the devices and reducing waste of materials.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据