Purified bentonite; Diffusion; Selenite; Ionic strength; Activation energy
资金
- [S24226021]
Selenium (Se) is an important element for assessing the safety of high-level waste disposal. In this study, the diffusion coefficients of selenite in purified bentonite were investigated. A Japanese purified sodium bentonite, Kunipia-F, which contains approximately 99 wt% montmorillonite, was used in this experiment. Bentonite powder was compacted into cylinders (diameter, 10 mm; height, 10 mm; dry density, 0.8-1.6 Mg m(-3)). Each compacted bentonite specimen was inserted into an acrylic resin column and saturated with 0.01 M-1.0 M of NaCl (aq.) for 30 days. One side of the bentonite was spiked with 10 mu L of tracer solution containing 0.13 M Na2SeO3 and it was kept at 10, 25, 40, or 55 degrees C for 1-29 days. The apparent diffusion coefficients of selenite in compacted bentonite were 2.5 x 10(-11) to 1.9 x 10(-13) m(2) s(-1) and decreased with the increase in dry density. The ionic strength showed no significant effect on the apparent diffusion coefficient of selenite for bentonite densities higher than 1.4 Mg m(-3). However, the apparent diffusion coefficients for 1 M NaCl were several times larger than those in 0.1 or 0.01 M NaCl for densities lower than 1.2 Mg m(-3). This increase in diffusion coefficient would be caused by a change in anion accessible porosity. The apparent diffusion coefficient would be explained by Archie's law and is proportional to exponentiation of porosity. It is desired to measure exact anion accessible porosity. The activation energy of selenite in purified bentonite was 20 +/- 4 kJ mol(-1) and was similar to the activation energies of oxo-anions in free water. This also indicates that selenite diffuses in free pore water in the bentonite. (C) 2015 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据