卷 74, 期 7, 页码 2479-2496出版社
SPRINGER
DOI: 10.1007/s00289-016-1850-9
关键词
Poly(ethylene terephthalate); Chain extender; Intrinsic viscosity; Rheological properties; Melt strength
资金
- Shanghai industry-university-research cooperation project [CXY-2014-023]
- Jiangsu province science and technology achievements transformation project [SBA2014010034]
A simple approach for preparing recycled poly(ethylene terephthalate) (r-PET) with excellent processability and melt strength has been developed in this research. To increase the intrinsic viscosity of r-PET, a two-step chain extension process using a combination of SAG-008 and tetraglycidyl-4,4'-diaminodiphenylmethane (TGDDM) was investigated. To evaluate the chain extension degree of the modified r-PET, its intrinsic viscosity (IV) and rheological properties were characterized, and found to be correlated to the long-chain branches and molecular weight. The results indicated that the combination of SAG-008 and TGDDM at the optimized conditions provided the highest IV of 1.18 dl/g while controlling the gel formation to a low value. The increases in storage modulus, loss modulus and complex viscosity revealed the enhancement of melt strength and viscoelasticity of r-PET. The differential scanning calorimetry results showed that the crystallinity was reduced with the addition of chain extenders. On the other hand, stepwise annealing method from room temperature to crystal melting temperature promoted the crystallization, which was confirmed by wide-angle X-ray diffraction measurement.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据