CHEMISTRY OF MATERIALS
卷 27, 期 23, 页码 7982-7989出版社
AMER CHEMICAL SOC
DOI: 10.1021/acs.chemmater.5b03296
关键词
-
资金
- National Research Foundation of Korea (NRF) [2014R1A2A1A11052829, 2015R1A2A2A04003160]
- Global Ph.D. Fellowship - National Research Foundation of Korea [NRF-2013H1A2A1033123, NRF-2013H1A2A1033278]
- National Research Foundation of Korea [2014R1A2A1A11052829, 2013H1A2A1033278, 2013H1A2A1033123, 2015R1A2A2A04003160] Funding Source: Korea Institute of Science & Technology Information (KISTI), National Science & Technology Information Service (NTIS)
An ultrathin supercapacitor electrode based on reduced graphene oxide (rGO) nanosheets is prepared using Layer-by-Layer (LbL) assembly. The rGO nanosheets functionalized with a conducting polymer, poly(3,4-ethylene dioxythiophene):poly(styrenesulfonate) (PEDOT:PSS), were assembled using a photo-cross-linkable diazoresin (DR). The unique photo-cross-linking property of the DR polymer the conversion of the ionic bonds in the LbL-assembled film to covalent bonds upon UV irradiation, significantly enhancing the overall electrochemical activity of the resulting ultrathin supercapacitor electrode. By UV/vis and Fourier transform infrared (FT-IR) spectroscopy measurements, we proved that decomposition of the diazonium group from DR, followed by covalent bond formation, contributed to the enhanced integrity of the adjacent interfaces within the multilayers. In particular, electrochemical measurements suggested that a charge transfer process is facilitated after cross-linking, which resulted in a considerable increase in the volumetric capacitance. The hybrid thin film of the rGO supercapacitor exhibited a capacitance of 354 F/cm(3) at a scan rate of 20 mV/s and maintained a capacitance of 300 F/cm(3) even at a high scan rate of 200 mV/s, thus outperforming many other thin film supercapacitors.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据