Influence of Zn-substitution on structural, magnetic, dielectric, and electric properties of Li-Ni-Cu ferrites

The polycrystalline Li0.15Ni0.6-xZnxCu0.1Fe2.15O4 ferrites are fabricated by the method of conventional solid-state reaction technique. The X-ray diffraction (XRD) confirms that the structure of the composition is a single-phase cubic spinel structure for all samples. The particle size of the compositions is varied from 36 to 52 nm. The lattice parameter and densities are found to increase with enhancing Zn content, as the ionic radius and atomic weight of Zn are greater than Ni. The porosity exhibits a decreasing trend. The average grain size determined using Field Emission Scanning Microscopy (FESEM) increases until x = 0.40, then declines. The Energy-Dispersive Spectroscopy (EDS) examination revealed that the percentage of obtained elements is well matched with the stoichiometric elements. The addition of Zn content acts as an accelerator for enhancing the value of the real part of initial permeability and the highest value is obtained (mu i' = 276) for the x = 0.40 sample, as well as the highest relative quality factor (RQF) of around 3000. The loss factor for the Zn substituted composition is nine times lower than for the parent composition. The optimum saturation magnetization of around 77.49 emu/g is found for the x = 0.40 sample. The maximum dielectric constant (epsilon' = 2.85 x 103) is found for x = 0.10 samples at 10 kHz. Further, from impedance studies, the non-Debye type dielectric relaxation is seen for the Zn-substituted samples. The observed region of the imaginary electric modulus peak signifies the transition of charge carrier mobility from a larger range to a short-range distance. The phenomenon of ac conductivity is attributed to the process of the small polaron hopping mechanism.

Automated summary

In this study, polycrystalline Li0.15Ni0.6-xZnxCu0.1Fe2.15O4 ferrites were prepared using a conventional solid-state reaction method. The addition of Zn increased the lattice parameter and densities, leading to improvements in the real part of initial permeability and relative quality factor. The replacement of Ni with Zn also resulted in lower loss factor and improved magnetic properties.